The new launched 1000W handheld laser welder from MRJ-Laser is equipped with air cooling system. Compared with previous welder device, it is significantly faster, easier to master and operate, and provides better and more uniform welding results on a wider variety of materials and thicknesses without distortion, edge gnawing or burn-through. The heat affected zone is greatly reduced, and the subsequent grinding and polishing required by traditional welding methods is also reduced, resulting in increased overall productivity, reduced scrap and lower cost per part.

The laser power of 1000W allows for quick selection of the right weld setting for different materials and thicknesses with an intuitive adjustment knob. With multi storeable presets and user-defined process parameters, novice welders can master welding operations with hours of training. Select stored modes provide up to 2500W of peak power for even greater welding capability.

Product features

Welding Methods and Materials

Recommended instrument parameter settings

The laser is generally used in continuous mode with a power ramp-up/down time of 500ms, which ensures a good forming effect at the beginning and end of the weld.

The larger the oscillation size of the welding head, the better the gap adaptation, but at the same time, the weaker the energy distribution; similarly, the higher the oscillation frequency, the lower the energy density. The recommended oscillation size range is 0.8~1.2mm and frequency range is 100~200HZ.

It is recommended to be in the focal position when welding 1mm thickness plates, and out of focus-1mm when welding 2 or 3mm thickness plates.

Use inert gas as shielding gas, argon or nitrogen is recommended, argon is better. The gas pressure is roughly 0.2MPa, too much pressure will blow away the molten If the pressure is too high, it will blow out the melt pool and increase the spatter, but if it is too low, it will not be effective. The gas out/off delay is set to 500ms to better protect the weld seam and weld head lens. The head lens.

The appropriate welding speed is 1 to 6 cm/s. Too low a speed results in a wide melt width and a large heat affected zone, which reduces the performance of the welded joint; too fast a speed is not easy to control.

It is recommended to weld steel thickness from 0 to 3 mm, aluminum and copper thickness from 0 to 2 mm. welding more than this thickness will deteriorate the shape of the weld and the performance of the joint.